鐵酸鈣渣系脫磷的研究

1、鐵酸鈣渣系脫磷的研究鐵酸鈣渣系脫磷的研究郭興敏韓其勇劉瀏丁容金振堅(北京科技大學)(鋼鐵研究總院)楊穎(鞍山鋼鐵(集團)公司)摘要通過1350℃、N2氣氛下，鐵酸鈣渣系對碳飽和FeCP合金的脫磷試驗，發(fā)現鐵酸鈣脫磷劑與氧化物脫磷劑相比，非脫磷途徑耗氧量少，且具有良好的脫磷動力學條件；CaF2添加量超過5%后，鐵酸二鈣比鐵酸一鈣的脫磷效果好，CaF2的適宜添加量是10%；攪拌加速了鐵液內的傳質過程，也導致提前出現回磷現象。關鍵詞關鍵詞脫

2、磷鐵酸鈣動力學STUDYOFDEPHOSPHIZATIONBYCALCIUMFERRITEFLUXESGUOXingminHANQiyong(UniversityofScienceTechnologyBeijing)LIULiuDINGRongJINZhenjian(CentralIronSteelResearchInstitute)YANGYing(AnshanIronSteel(Group)Company)ABSTRACTDepho

3、sphizationexperimentsofCsaturatedFeCPalloybycalciumferritefluxeshasbeenstudiedat1350℃underaN2atmosphere.Itwasfoundthatwithcalciumferritefluxeslessoxygenisconsumedfnondephosphizationreactionsthekiicconditionsofdephosphiza

4、tionarebettercomparingwiththecaseswhereotherfluxesareusedthedephosphizationeffectofdicalciumferriteisbetterthanthatofmonocalciumferritewhentheCaF2contentinfluxesismethan5percentthesuitablecontentofCaF2is10percentthemecha

5、nicalstirringincreasestherateofmasstransferinmoltenironbutalsoincreasestherephosphizationratesimultaneously.KEYWDSdephosphizationcalciumferritekiics1前言前言石灰系脫磷劑被廣泛地應用于鐵水預處理，對其脫磷熱力學性質以及工藝操作方面已有報道［1～3］。研究結果表明，脫磷過程不但要求具01323

6、.3466.6610.0001422.0462.9615.0001520.7459.2620.00實驗時，在通入N2、1350℃恒溫的碳管爐內放入盛有FeCP合金的石墨坩堝，熔清后迅速把粉狀脫磷劑放在鐵液之上，開始記錄脫磷反應時間。以適當的時間間隔，用石英管吸取0.5～1.0g鐵樣，并用鐵鉻合金棒粘取少量的渣樣，直至回磷為止。鐵液中磷的含量和渣中全鐵(TFe)、二價鐵(Fe2)含量，分別采用磷鉬釩酸光度法和重鉻酸鉀法進行分析。3實驗結果

7、與討論實驗結果與討論鐵酸鈣脫磷劑和氧化物脫磷劑脫磷過程的比較如圖1所示，從脫磷規(guī)律上看兩者是一致的。反應初始階段，［P］隨反應時間增加而降低，直到最小值［P］min；t＞t［P］min后，［P］隨反應時間而增加，出現回磷現象。在脫磷效果［P］min上，鐵酸鈣脫磷劑比氧化物脫磷劑的脫磷能力強，這可以說是脫磷機理不同引起的。雖然兩種脫磷劑的化學組成相同，但熔化前以分子形態(tài)存在時，兩者是不同物質；熔化后以離子形態(tài)存在時圖1脫磷過程中鐵液內磷含